PVC Compounds - Various Grades

We are a leading manufacturer of premium PVC cable compounds for wide application in the cable PVC Compounds - Various Grades industry. Our range of compounds is available for numerous applications for Power Cables, Control and Instrumentation Cables, Winding wire for submersible Pump Motor, Three Core Flat Cables, Appliance Cords, etc. Our PVC compounds are available for both insulation and sheathing.

These compounds are also used for House Wiring, Telecom Cables, Automotive Cables, etc. All our products & PVC compounds conform to standards as per ISO standards. Our compounds are manufactured from top quality Colour Master-batches & are weather resistant, UV resistant, non-migrant, non-blooming.

Specification for PVC compound (Sheathing Grades) Spec ref.: IS 5831/1984

Test

Test Carried Out

Unit

Req. Value

Observed

Value

 

S. no

PVC Grades

 

 

RC-415

RC-06

RC-060

1.

Specific Gravity

-

-

1.38

1.48

1.50

2.

Thermal Stability

Minutes

40

60

85

50

3.

Tensile Strength without ageing

N/ Sq.mm

12.5

14

16

50

4.

Tensile Strength after ageing for 7 days

N/Sq.mm

12.5

14

16

14

5.

Variation in Tensile Strength

%

± 20

±7

± 6

± 10

6.

Elongation at Break without ageing

%

150

240

230

200

7.

Elongation at Break after ageing for 7 days

%

150

240

230

200

8.

Variation in Elongation at break

%

± 20

8

6

10

9.

Loss of Mass

Ma/cm²

2

1.7

1.2 ± 0.5

1.5 ±0.25

10.

Hardness

Shore A

2

73

85

88



Specification for PVC compound (Insulation grades) Spec. Ref.: IS 8531/1984

Test

Test Carried Out

Unit

Req. Value

Observed

Value

 

S. no

PVC Grades

 

 

RC-41

RC-04 (IS)

RC-06H

1.

Specific Gravity

-

-

1.37

1.48

1.50

2.

Thermal Stability

Minutes

80

110

95

80

3.

Volume Resistivity at 27 Dec. C

Ohm/cm

1x1013

10x1014

7.5x1013

4x1013

4.

Tensile Strength without ageing

N/Sq.mm

12.5

17

15

13.5

5

Tensile Strength after ageing for 7 days

N/Sq.mm

12.5

17

15

13.5

6.

Variation in Tensile Strength

%

± 20

5

11

12

7.

Elongation at Break without ageing

%

150

250

225

200

8.

Elongation at Break after ageing for 7 days

%

150

250

225

200

9.

Variation in Elongation at break

%

± 20

±5

±8

±10

10

Loss of Mass

Ma/cm²

2

0.8

1.2

1.4

11.

Hardness

Shore A

-

90

88

90



Note :

* The Compound specifications are subject to change without prior notice
* Information provided in comp. Specification are true to the best of our knowledge
* Any liability in connection with data and recommendation is disclaimed since the conditions of use are beyond our control.
* It is advisable to store the materials in cool and dry place and for better results pre-heating of the material is recommended.

About Us

From modest beginning in 1995 when our first unit of the manufacturing of PVC Cables was set up SA has grown from strength to strength over the years.

We have been expanding and diversifying rapidly and today we have been recognized as one of the leading and fast expanding company in PVC Cables ,PVC Pipe manufacturing, PVC Casing Capping/ Trunking, PVC Compound, Copper/ Aluminium Wire Drawing
Read More

Testimonials

It has been a great pleasure doing business with you. Your Company should be forever grateful to have such polite and professional staff members working for them. You were able to handle my order with great ease and professionalism your experience and politeness will certainly make me recommend others to do business with your company in the future.

Alba Group
Managing Director